<i id="jvnj9"></i><sub id="jvnj9"></sub>

          <dfn id="jvnj9"><b id="jvnj9"></b></dfn>

          <output id="jvnj9"></output>

                  <b id="jvnj9"><cite id="jvnj9"><big id="jvnj9"></big></cite></b>
                    <th id="jvnj9"><b id="jvnj9"></b></th>

                    <big id="jvnj9"><i id="jvnj9"></i></big><ruby id="jvnj9"></ruby>

                      <ins id="jvnj9"></ins>

                        <i id="jvnj9"></i><b id="jvnj9"></b>

                        <b id="jvnj9"></b>

                        <form id="jvnj9"><var id="jvnj9"></var></form>

                            <em id="jvnj9"><del id="jvnj9"></del></em>
                              <i id="jvnj9"><output id="jvnj9"><progress id="jvnj9"></progress></output></i>
                              <nobr id="jvnj9"></nobr>

                              電話:0769-85371908

                              塑料模具鋼
                              日2019韩色老司机,成黄色人五月天,小系列视频资源,动精品漫久久
                              您現在的位置: 網站首頁 - 產品中心

                              進口維羅納 1.2738

                              ①主要性能及應用

                              1.22738的主要特點是優秀的硬化深度,優良的可加工性,拋光和蝕刻性能佳。主要用于大中型塑膠模具。

                              可施以氮化處理獲得更高的耐磨性能。                                           

                              主要適用于:注塑模,熱塑擠壓模,橡膠模具,模架等的生產。


                              ②對應的標準

                              UNI      W.Nr      DIN                            AFNOR          AISI/SAE     BS

                              -          1.2738    40CrMnNiMo8-6-4    40CMND8     P20+Ni       P20+Ni


                              ③化學成份

                              C            Mn        Si          Cr          Mo       Ni       V       P+S

                              0.35       1.30       0.20      1.80       0.15      0.90

                              0.45       1.60       0.40      2.10       0.25      1.20             0.015


                              ④相變溫度

                              Ac1      860℃

                              Ms       340℃


                              ⑤交貨硬度

                              預硬和回火:HB300~340


                              ⑥熱處理

                              退火

                              ●加熱至710~740℃,保溫至少3小時

                              ●緩慢爐冷至600℃


                              去應力

                              ●在機加工后最終熱處理之前進行

                              ●加熱至530~580℃保溫2小時


                              預硬

                              ●加熱至500~550℃

                              ●在840~880℃奧氏體化

                              ●油冷或熱浴冷至300~230℃,然后根據模具尺寸選擇合適的溫度油冷

                              ●淬火硬度52~54HRC


                              回火

                              ●淬火冷卻至60~80℃立即進行

                              ●根據不同的硬度加熱至500~600℃后保溫至少2小時

                              ●空冷


                              ⑦C.C.T   曲線

                              圖片5.png

                              ⑧回火 曲線

                              圖片6.png